PC/ABS alloy is an excellent engineering plastic with great performance in impact resistance,heat resistance, chemical resistance and dimensional stability. It can bewidely used in automotive panels, automotive parts, mobile phone shell, eclectictools, and house hold appliances and so on.
Performance | Test Standard (ASTM) | Test Condition | Unit | High Impact and Fluidity Series | Heat Resistant Series | |
Feature | High impact and fluidity | High-heat resistant | ||||
Physical properties | Density | D-792 |
| g/cm3 | 1.12 | 1.15 |
Melt index | D-1238 | 260℃,3.8kg | g/10min | 14 | 7 | |
Mold shrinkage rate | D-955 |
| % | 0.5-0.7 | 0.5-0.7 | |
Mechanical properties | Tensile strength | D-638 |
| MPa | 53 | 52 |
Elongation at break | D-638 |
| % | 60 | 100 | |
Bending strength | D-790 |
| MPa | 78 | 77 | |
Bending modulus | D-790 |
| MPa | 2400 | 2300 | |
Notched cantilever beam impact strength | D-256 | 6.4 mm | J/m | 690 | 640 | |
3.2 mm | J/m | 810 | 730 | |||
Thermal properties | Heat distortion temperature | D-648 | 1.82 MPa | ℃ | 96 | 110 |
Vicat softening temperature | D-1525 | 50N,50℃/h | ℃ | 106 | 127 | |
Flame retardant | UL-94 | 1.6 mm | Class | HB | HB |
Note: 1. The abovedata were all typical values and shall not be considered as product specifications orguarantee.
2. The above data were tested on injectedsample piece at 23℃, 50% humidity condition.